Durability of Thermal Renders with Lightweight and Thermal Insulating Aggregates: Regranulated Expanded Cork, Silica

André Morgado1, António Soares1, Inês Flores-Colen1

  • 1CERIS, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa, Portugal.

Gels (Basel, Switzerland)
|April 3, 2021
PubMed

Keywords:
accelerated aging cyclesexpanded polystyrenefreeze/thaw cycleslightweight aggregateregranulated expanded corksilica aerogelthermal render

More Related Videos

Preparation of Biopolymer Aerogels Using Green Solvents08:13

Preparation of Biopolymer Aerogels Using Green Solvents

Published on: July 4, 2016

17.9K
Aesthetically Enhanced Silica Aerogel Via Incorporation of Laser Etching and Dyes08:21

Aesthetically Enhanced Silica Aerogel Via Incorporation of Laser Etching and Dyes

Published on: March 12, 2021

3.1K

Related Concept Videos

Thermal Insulation in Masonry Walls01:22

Thermal Insulation in Masonry Walls

In hot, dry climates, the thermal mass of masonry walls can be beneficial, absorbing heat during the day and releasing it at night, thereby stabilizing indoor temperatures. However, in most other climates, additional insulation is necessary to enhance thermal resistance.
External insulation can be applied using an Exterior Insulation and Finish System (EIFS), which involves affixing panels of plastic foam to the wall and covering them with a polymeric stucco reinforced with glass fiber mesh....
282
Pozzolans01:21

Pozzolans

Pozzolans are siliceous or aluminous materials blended with Portland cement. They interact with the calcium hydroxide produced during the hydration of Portland cement and contribute to improved strength and durability of concrete. The pozzolanic activity, a measure of a pozzolan's effectiveness, is typically assessed using the strength activity index, as defined in ASTM C 618-93, which calculates the ratio of the compressive strength of cement mixtures with and without pozzolan.
Fly ash is...
288
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate...
240
Brick Durability, Strength, and Appearance01:15

Brick Durability, Strength, and Appearance

Brick durability, strength, and appearance are crucial factors in construction, influencing the choice of bricks for specific applications. The process of freeze-thaw, for instance, significantly affects brick durability. This phenomenon occurs when water absorbed by a brick expands as it freezes, potentially causing damage when it melts and refreezes. Bricks are graded for durability: SW-grade bricks are the most durable, offering high strength and low water absorption, followed by MW-grade...
473
Frost Resistant Concrete01:29

Frost Resistant Concrete

Concrete's susceptibility to frost damage during freeze-thaw cycles demands strategic measures to enhance its frost resistance. Employing techniques like air entrainment, adjusting the water-cement ratio, proper curing, and selecting appropriate aggregates are essential.
Introducing microscopic air bubbles into the concrete mix through air entrainment creates small voids that accommodate ice expansion, thereby reducing internal pressures and preventing cracking. The optimal amount of...
226
Fiber Reinforced Concrete01:22

Fiber Reinforced Concrete

Fiber-reinforced concrete significantly enhances the structural and nonstructural properties of traditional concrete by incorporating fibers like steel, glass, and polymers. These fibers, varying from natural ones such as sisal and cellulose to manufactured ones like polypropylene and Kevlar, are mixed into hydraulic cement with aggregates. Steel fibers, often preferred for their robustness, contribute to improved ductility, toughness, and post-cracking performance. The concrete is classified...
190