Effects of titanium with different micro/nano structures on the ability of osteoblasts to resist oxidative stress

Excessive accumulation of oxidative intermediates in the elderly significantly aggravates bone degradation and hinders the osseointegration of topological titanium (Ti) implants. Thus, it is of great significance to evaluate the antioxidant and osteoinduction capabilities of various nano, micro or micro/nano-composite structures under oxidative stress (OS) microenvironment. In this study, we discovered that 110 nm titania nanotubes (TNTs) enhanced the adsorption of fibronectin (FN) proteins onto smooth and rough titanium surfaces to varying degrees. Compared with Ti and 30 nm TNTs (T₃₀) groups, cells on 110 nm TNTs (T₁₁₀), microstructure/30 nm TNTs (M₃₀) and microstructure/110 nm TNTs (M₁₁₀) had smaller area, lower reactive oxygen species (ROS), and better proliferation/osteogenic differentiation abilities under OS condition, but there was no significant difference among the three groups. In addition, combined with our previous study, we suggested that T₁₁₀, M₃₀ and M₁₁₀ resistance to OS was also strongly associated with the high expression of FN-receptor integrin α5 or β1. All the findings indicated that the micro/nano-composed structures (M₃₀ & M₁₁₀) had similar anti-oxidation and osteogenesis abilities to T₁₁₀, which provided guidance for the application of different titanium implants with different topologies in the elderly.