Chitosan derivatives-based films as pH-sensitive drug delivery systems with enhanced antioxidant and antibacterial...

The purpose of this study was to develop and characterize chitosan (Ch)-based films incorporated with varying molecular weight (Mw) and acetylation degree (AD) chitosan-depolymerization-products (CDP), to be applied as drug delivery materials. As compared to Ch-film, optical and antioxidant potentials of Ch/CDP-based films were improved, particularly using low Mw and AD-CDP. Whereas, films water resistance, mechanical and antibacterial properties increased as CDP-Mw increased and AD decreased. For the thermal and swelling behaviors, better values were obtained using higher Mw and AD-CDP. Further, to assess their in vitro ciprofloxacin (CFX)-release behavior, loaded-CFX Ch/CDP-based films, crosslinked using glutaraldehyde, were prepared. Expect of elongation at break, crosslinked CFX-loaded films showed increased optical, water resistance, tensile strength and thermal properties, as compared to unloaded films. The CFX-release profiles indicated that a slower and sustained release was observed, particularly when using lower Mw and AD-CDP, and mainly for the crosslinked films during 48 h. These films can release CFX for up to 54% in 6 and 24 h, at pH 1.2 and 7.4, respectively. Through this study, novel biodegradable, swellable and pH-sensitive crosslinked Ch/CDP-based films may be considered as suitable and promising drug delivery systems.