Chitosan/alginate/hyaluronic acid polyelectrolyte composite sponges crosslinked with genipin for wound dressing
Xin Meng1, Yang Lu1, Ying Gao1
1Key Laboratory of Industrial Microbiology, Ministry of Education, College of Biotechnology, Tianjin University of Science and Technology, China International Science and Technology Cooperation Base of Food Nutrition/Safety and Medicinal Chemistry, Tianjin 300457, PR China.
Abstract:
Wound dressing composed of polyelectrolyte complexes (PECs), based on chitosan/alginate/hyaluronic acid (CS/ALG/HYA) crosslinked by genipin, was prepared by freeze-dried molding. Genipin as excellent natural biological crosslinker was chose for high biocompatibility and improving mechanical properties of materials. The CS/ALG/HYA sponges (CAHSs) were characterized by FTIR, XRD, DSC and SEM. Porosity, swelling behavior and mechanical properties and in vitro degradation of CAHSs were investigated. The cytotoxicity assay was carried out on HUVEC cells in vitro and the result proves the good biocompatibility of CAHSs. Hemolysis tests indicated that the prepared CAHSs were non-hemolytic material (hemolysis ratio < 5%, no cytotoxicity). PT and aPPT coagulation tests demonstrated that CAHS2 and CAHS3 could both activate the extrinsic and intrinsic coagulation pathway and thus accelerated blood coagulation. Further, in a rat full-thickness wounds model, the CAHS2 sponge significantly facilitates wound closure compared to other groups. CAHSs exhibited adjustable physical, mechanical and biological properties. Thus, the chitosan-based polyelectrolyte composite sponges exhibit great potential as promising wound dressings.