The nanostructure of rod-like ascorbyl dipalmitate nanoparticles stabilized by a small amount of DSPE-PEG

Previously, we reported the formation of 100-200 nm disk- and tube-like nanoparticles by hydration of _L-ascorbyl 2,6-dipalmitate (ASC-DP) and distearoylphosphatidylethanolamine polyethylene glycol 2000 (DSPE-PEG) films prepared at an initial molar ratio of 2:1. This study investigated the feasibility of nanoparticle formation with higher ASC-DP loading. Although particle size distribution determined by dynamic light scattering showed a multimodal pattern including micro-sized particles at a molar ratio of 3:1, the mean particle size gradually decreased with a further increased molar ratio. Homogeneous ca. 240 nm nanoparticles with a unimodal size distribution were obtained at a molar ratio of 10:1. FE-TEM showed that the nanoparticles at a molar ratio of 10:1 were rod-shaped with a diameter of ca. 100 nm and a length of ca. 300 nm. After centrifugation, X-ray analysis of the nanoparticle precipitates showed that these rod-like nanoparticles were composed of a series of lamellar structures with 3.7 nm repeated units. The molar ratio of ASC-DP/DSPE-PEG in the nanoparticle precipitates determined by ¹H NMR measurements was 68.8:1. The rod-like nanoparticles should be composed of a core-shell structure, where a small amount of DSPE-PEG covers the lamellar structure of ASC-DP. Further increase in the ASC-DP/DSPE-PEG molar ratio over 33:1 no longer provided nanoparticles. Hence, to prepare a stable ASC-DP nanoparticle suspension, it is necessary to prepare ASC-DP/DSPE-PEG films containing at least 3 mol% DSPE-PEG.