Synthesis of Vanadium Doped Lanthanum Bismuthate Nanorods for Enhanced Photocatalytic Activity

Vanadium doped lanthanum bismuthate nanorods with vanadium ratio of 1%, 3%, 5% and 10 wt.% were fabricated through the hydrothermal method using sodium orthovanadate as vanadium source. Vanadium doped lanthanum bismuthate nanorod products were analyzed by scanning electron microscopy, X-ray diffraction pattern and diffuse reflection spectrum. X-ray diffraction patterns show that vanadium in the vanadium doped lanthanum bismuthate nanorods exists as triclinic Bi₂₃V₄O_44.5 and monoclinic LaVO₄ phases. Scanning electron microscopy observations show that the size and micro-morphology of the vanadium doped products are closely relative to the vanadium mass ratio. The length of the vanadium doped nanorods decreases and the morphology changes from nanorods to irregular nanoparticles with increasing the vanadium mass ratio. Solid UV-vis diffuse reflectance measurement shows that the bandgap value of the doped lanthanum bismuthate nanorods is narrowed from 2.37 eV to 2.25 eV after the vanadium doping ratio is increased from 1% to 10%. The doped lanthanum bismuthate nanorods illustrate enhanced photocatalytic performance for methylene orange (MO) removal with the irradiation of sunlight. The catalytic performance for MO removal depends on the irradiation time, vanadium content and dosage of the nanorods. The doped lanthanum bismuthate nanorods with the vanadium mass ratio of 10% possess the best MO catalytic degradation performance.