Pt-based (Zn, Cu) nanodendrites with enhanced catalytic efficiency and durability toward methanol electro-oxidation...

Pt-based alloy nanomaterials with nanodendrites (NDs) structures are efficient electrocatalysts for methanol oxidation reaction (MOR), however their durability is greatly limited by the issue of transition metals dissolution. In this work, a facile trace Ir-doping strategy was proposed to fabricate Ir-PtZn and Ir-PtCu alloy NDs catalysts in aqueous medium, which significantly improved the electrocatalytic activity and durability for MOR. The as-prepared Ir-PtZn/Cu NDs catalysts showed distinct dendrites structures with the averaged diameter of 4.1 nm, and trace Ir doping subsequently improved the utilization of Pt atoms and promoted the oxidation efficiency of methanol. The electrochemical characterizations further demonstrated that the obtained Ir-PtZn/Cu NDs possessed enhanced mass activities of nearly 1.23 and 1.28-fold higher than those of undoped PtZn and PtCu, and approximately 2.35 and 2.67-fold higher than that of Pt/C in acid medium. More excitingly, after long-term durability test, the proposed Ir-PtZn and Ir-PtCu NDs still retained about 88.9% and 91.6% of its initial mass activities, which further highlights the key role of Ir-doping in determining catalyst performance. This work suggests that trace Ir-doping engineering could be a promising way to develop advanced electrocatalysts toward MOR for direct methanol fuel cell (DMFC) applications.