Improved Hydrogenation Kinetics of TiMn_1.52 Alloy Coated with Palladium through Electroless Deposition

The deterioration of hydrogen charging performances resulting from the surface chemical action of electrophilic gases such as CO₂ is one of the prevailing drawbacks of TiMn_1.52 materials. In this study, we report the effect of autocatalytic Pd deposition on the morphology, structure, and hydrogenation kinetics of TiMn_1.52 alloy. Both the uncoated and Pd-coated materials were characterized using scanning electron microscopy/energy dispersive spectroscopy (SEM/EDS) and X-ray diffraction (XRD). XRD analyses indicated that TiMn_1.52 alloy contains C14-type Laves phase without any second phase, while the SEM images, together with a particle size distribution histogram, showed a smooth non-porous surface with irregular-shaped particles ranging in size from 1 to 8 µm. The XRD pattern of Pd-coated alloy revealed that C14-type Laves phase was still maintained upon Pd deposition. This was further supported by calculated crystallite size of 29 nm for both materials. Furthermore, a Sieverts-type apparatus was used to study the kinetics of the alloys after pre-exposure to air and upon vacuum heating at 300 °C. The Pd-coated AB₂ alloy exhibited good coating quality as confirmed by EDS with enhanced hydrogen absorption kinetics, even without activation. This is attributed to improved surface tolerance and a hydrogen spillover mechanism, facilitated by Pd nanoparticles. Vacuum heating at 300 °C resulted in removal of surface barriers and showed improved hydrogen absorption performances for both coated and uncoated alloys.