Nanocomposite Polymer Electrolytes of Sodium Alginate and Montmorillonite Clay

Nanocomposite polymer electrolytes (NPEs) were synthesized using sodium alginate (Alg) and either sodium (SCa-3-Na⁺)- or lithium (SCa-3-Li⁺)-modified montmorillonite clays. The samples were characterized by structural, optical, and electrical properties. SCa-3-Na⁺ and SCa-3-Li⁺ clays' X-ray structural analyses revealed peaks at 2θ = 7.2° and 6.7° that corresponded to the interlamellar distances of 12.3 and 12.8 Å, respectively. Alg-based NPEs X-ray diffractograms showed exfoliated structures for samples with low clay percentages. The increase of clay content promoted the formation of intercalated structures. Electrochemical Impedance Spectroscopy revealed that Alg-based NPEs with 5 wt% of SCa-3-Na⁺ clay presented the highest conductivity of 1.96 × 10^-2 S/cm², and Alg with 10 wt% of SCa-3-Li⁺ showed conductivity of 1.30 × 10^-2 S/cm², both measured at 70 °C. From UV-Vis spectroscopy, it was possible to infer that increasing concentration of clay promoted a decrease of the samples' transmittance and, consequently, an increase of their reflectance.