Mechanical and Microstructural Properties of Ordinary Concrete with High Additions of Crushed Glass

This study investigates the use of crushed glass waste as partial cement replacement in ordinary concretes. Six concrete mixes were designed and prepared: a reference without substitution and five substitution percentages of crushed glass waste ranging from 5% to 25%. The made concrete mix design underwent different tests, namely: slump test, mechanical strength, thermogravimetric analysis (TGA), X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) determination and finally, water porosimetry, in order to evaluate the influence of the use of crushed glass waste on the properties of fresh and hardened concrete. Mechanical strengths results show that the use of 15% of the crushed glass waste improves the mechanical strength. TGA analysis confirms this result by highlighting a higher hydration degree. The latter contributes to the reduction of the porosity and, consequently, the mechanical strength increases. Also, it can be caused by the increasing amount of chromium which, if added a little, accelerates the hydration of C3S and leads to an increase of the mechanical strength. The BET technique and porosimetry tests showed that the use of crushed glass waste reduces the global porosity of concrete. This is due to the filling effect of the glass powder.