Bioactivity of PEEK GRF30 and Ti6Al4V SLM in Simulated Body Fluid and Hank's Balanced Salt Solution

In recent years, scientists have defined two main paths for orthopedic implant fabrication: searching for new materials with properties closest to natural bone in order to reduce the stress-shielding effect or creating individually adapted geometry of the implant with the use and Rapid Prototyping methods. Therefore, materials such as PEEK GRF30 and Ti6Al4V selective laser melting (SLM) are of interest. They are defined as materials suitable for implants, however, the knowledge of their bioactivity, a feature which is one of the most desirable properties of biomaterials, is still insufficient. Using Simulated Body Fluid and Hank's Balanced Salt Solution, the bioactivity of PEEK GRF30 and Ti6Al4V SLM was assessed, as well as commercial Ti6Al4V as a reference material. Ten cylindrical samples of each material were prepared and immersed in solutions per period from 2 to 28 days at 37 °C. Optical analysis of the changes on the examined surfaces suggested that right after 2-day crystals with different morphologies were formed on each material. Further analysis of the chemical composition of the altered surfaces confirmed the formation of a calcium phosphate layer on them, however, the Ca/P ratio was slightly different from 1.67. On the basis of the obtained results, it can be concluded that both PEEK GRF30 and Ti6Al4V SLM are characterized by appropriate-comparable to Ti6Al4V-bioactivity.