Mechanism confirmation of organofunctional silanes modified sodium silicate/polyurethane composites for remarkably...

Hybrid reinforced sodium silicate/polyurethane (SS/PU) composites mainly derived from low-cost SS and polyisocyanate are produced by a one-step method based on the addition of 3-chloropropyltrimethoxysilane (CTS). The wettability of SS on PU substrate surface is much improved as CTS content increases from 0.0 to 3.5 wt%. Furthermore, with 2.5 wt% of CTS optimal addition, the fracture surface morphology and elemental composition of the resulting SS/PU composites are characterized, as well as mechanical properties, chemical structure and thermal properties. The results indicate that the CTS forms multiple physical and chemical interactions with the SS/PU composites to induce an optimized organic-inorganic hybrid network structure thus achieving simultaneous improvement of compressive strength, flexural strength, flexural modulus and fracture toughness of the SS/PU composites, with the improvement of 12.9%, 6.6%, 17.5% and 9.7%, respectively. Moreover, a reasonable mechanism explanation for CTS modified SS/PU composites is confirmed. Additionally, the high interface areas of the organic-inorganic phase and the active crosslinking effect of the CTS are the main factors to determine the curing process of the SS/PU composites.