Microshear Bond Strength of Nanoparticle-Incorporated Conventional and Resin-Modified Glass Ionomer to
Zahra Fattah1, Zahra Jowkar1, Safoora Rezaeian1
1Oral and Dental Disease Research Center, Department of Operative Dentistry, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.
Abstract:
The purpose of this study was to assess the influence of three different types of nanoparticles (silver (SNPs), titanium dioxide (TNPs), and zinc oxide (ZNPs)) on the microshear bond strength of conventional glass ionomer cement (CGIC) and resin-modified glass ionomer cement based on whether CGIC or RMGIC is used with four subgroups (based on the incorporation of SNPs, ZNPs, and TNPs in addition to a control subgroup) (n = 12) as follows: CGIC, CGIC + TNP, CGIC + ZNP, CGIC + SNP, RMGIC, RMGIC + TNP, RMGIC + ZNP, and RMGIC + SNP. After 24 hours, the μSBS of specimens was tested and the obtained data were analyzed using two-way ANOVA and Tukey's HSD test. The obtained results showed that the incorporation of TNPs in two glass ionomers was not statistically significant compared with the control subgroups (p > 0.05). In the first group, the highest and lowest mean μSBS were, respectively, observed in the CGIC + SNP subgroup and CGIC + ZNP subgroup. In the second group, RMGIC + ZNP and RMGIC + SNP, respectively, showed the highest and lowest mean μSBS compared to the other subgroups. According to the results, it can be concluded that TNPs can be incorporated into both CGIC and RMGIC without compromising the bond strength of glass ionomers. SNPs and ZNPs can be, respectively, added to CGICs and RMGICs to improve the bond strength of the restoration.