The effect of different storage media on the monomer elution and hardness of CAD/CAM composite blocks
Related Experiment Video
Updated: Nov 6, 2025
Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
Rasha A Alamoush1, Rehana Sung2, Julian D Satterthwaite3
1Prosthodontics Department, University of Jordan, Amman, Jordan; Dentistry, School of Medical Sciences, The University of Manchester, Manchester, UK.
Objective:
This study aimed to assess the effect of different storage media on the hardness and monomer elution of CAD/CAM composite blocks.
Methods:
Five resin-composite blocks (RCB), one polymer-infiltrated ceramic network (PICN) block (Enamic (EN)), one ceramic-filled poly ether ether ketone (PEEK) block (Dentokeep (DK)), and one feldspathic ceramic block. Microhardness was measured using a Vickers indenter tester (FM-700, Future Tech Corp., Japan). In addition 4 conventional resin-composites were investigated for monomer elution using high performance liquid chromatography (HPLC) after storage in different media for 3 months. The data were analysed by three-way ANOVA, two-way ANOVA, one-way ANOVA, Tukey's post hoc test and the independent t-test (α=0.05 for all tests).
Results:
The specimens stored in the water had a hardness reduction ranging from 0.9% to 24.4%. In artificial saliva, the specimens had a hardness reduction ranging from 2.8% to 23.2%. The hardness reduction percentage in 75% Ethanol/Water (E/W) ranged between 3.8% and 35.3%. All materials, except GR (resin-composite block) and DK (Polyetheretherketone (PEEK)), showed a variable extent of monomer elution into 75% E/W with significantly higher amounts eluted from conventional composites. GRA and GND (conventional resin-composites) eluted TEGDMA in artificial saliva and GRA eluted TEGDMA in water.
Significance:
The hardness of CAD/CAM composite blocks was affected by different storage media, and they were not as stable as ceramic, with PICN exhibited superior hardness stability to all of the resin-composite blocks in all the storage media and was comparable to ceramic block. The hardness reduction percentage of the CAD/CAM composite blocks was influenced by the filler loading and resin-matrix composition.Minimal or no monomer elution from CAD/CAM blocks was detected.