Development of oxidized hydroxyethyl cellulose-based hydrogel enabling unique mechanical, transparent and...

With the development of smart devices, higher requirements are put forward for the stimuli-responsive materials. Stimuli-hydrogels as one kind of stimuli-responsive materials with hydrophilicity, demonstrate huge potential in developing intelligent devices for biomedical application. On this basis, we herein report that a sample method was devised to develop a novel composite hydrogel mainly based on oxidized hydroxyethyl cellulose and allyl co-polymer. Subsequently, a series of tests toward this oxidized hydroxyethyl cellulose-based hydrogel due to its structure and performance was applied. Here, the oxidized hydroxyethyl cellulose molecular chains were used as biomacromolecule templates to form Schiff base, borate and hydrogen bonds to obtain unique mechanical properties (fast recovery with almost no-hysteresis and remarkable compressive capacity), while a double bond functionalized spirooxazine (allyl spirooxazine derivative) was applied to endow photo- and pH sensitivity to the oxidized hydroxyethyl cellulose-based transparent hydrogel (T% = 93%) substrate. Furthermore, the oxidized hydroxyethyl cellulose-based hydrogel did exhibit good pH environment adaptability and noncytotoxicity in vitro test. Based on the advanced characteristics, the designed oxidized hydroxyethyl cellulose-based hydrogel has potential applications prospect in the development of safe, fashionable and pH- detectable contact lenses, thereby providing a new strategy for the development of smart, stylish contact lenses.