Novel SeS2-loaded Co MOF with Au@PANI comprised electroanalytical molecularly imprinted polymer-based disposable...

An SeS₂-loaded Co MOF and Au@PANI nanocomposite comprising the base matrix of the electrode was developed with electropolymerized molecularly imprinted polymer (MIP) consisting of p-aminobenzoic acid (PABA) and patulin (PT) to detect PT molecules based on the PT imprinted cavities. SeS₂@Co MOF and Au@PANI were synthesized using hydrothermal synthesis and interfacial polymerization strategies, respectively. A suitable functional monomer to fabricate the MIP platform was selected using the density functional theory (DFT/M06-2X method). Higher electrochemical active surface area (0.985 cm² which is 6.99 times higher than the bare SPE) and a lower charge transfer resistance (R_ct = 27.8 Ω) at the MIP/Au@PANI/SeS₂@Co MOF electrode was achieved based on the higher number of adsorptive sites and enhanced conductivity (electron transfer rate constant (k_s = 3.24 × 10^-3 s^-1) of the sensing platform. The fabricated MIP sensor performance was studied in 10 mM PBS (pH = 6.4), where an improved detection limit (0.66 pM) for PT and a broad logarithmic linear dynamic range (0.001-100 nM) were both observed. The sensor possessed higher selectivity (Imprinting factor = 15.4 for PT), excellent reusability (%RSD of 10 cycles = 2.49%), high storage stability (6.7% lost after 35 days), and robust reproducibility (%RSD = 3.22%) The as-prepared MIP-based PT sensor was applied to detect PT in a real-time apple juice sample (10% diluted with PBS) with a recovery % ranging from 94.5 to 106.4%. The proposed sensor possesses great advantages in terms of cost-effectiveness, providing a simple detection strategy for long-term storage stability, and reversible cycle measurements.