Statistical models for estimating the uniaxial compressive strength and elastic modulus of rocks from different

Related Experiment Video

Updated: Nov 5, 2025

Atomic Force Microscopy Cantilever-Based Nanoindentation: Mechanical Property Measurements at the Nanoscale in Air and Fluid
08:58

Atomic Force Microscopy Cantilever-Based Nanoindentation: Mechanical Property Measurements at the Nanoscale in Air and Fluid

Published on: December 2, 2022

3.3K

Ahmet Teymen1

  • 1Department of Mining Engineering, Niğde Ömer Halisdemir University, 51240 Niğde, Turkey.

Heliyon
|May 19, 2021
PubMed

Keywords:
Brinell hardnessIndentation hardness indexMultiple regressionSchmidt hammer hardnessShore scleroscope hardnessVickers hardness

More Related Videos

A Uniaxial Compression Experiment with CO2-Bearing Coal Using a Visualized and Constant-Volume Gas-Solid Coupling Test System10:27

A Uniaxial Compression Experiment with CO2-Bearing Coal Using a Visualized and Constant-Volume Gas-Solid Coupling Test System

Published on: June 12, 2019

8.8K
Biomechanical Characterization of Human Soft Tissues Using Indentation and Tensile Testing07:07

Biomechanical Characterization of Human Soft Tissues Using Indentation and Tensile Testing

Published on: December 13, 2016

32.3K

Related Concept Videos

Elasticity in Concrete01:20

Elasticity in Concrete

Upon subjecting concrete to moderate or high uniaxial compressive or tensile stresses, the strain response is non-linear relative to the stress applied. As the stress is removed, the resulting stress-strain curve deviates from the original path traced during loading, creating a hysteresis loop, indicative of the concrete's non-linear and non-elastic properties. Typically, a material's modulus of elasticity, which is a measure of the material's stiffness, is inferred from the linear...
191
Strain and Elastic Modulus01:15

Strain and Elastic Modulus

The quantity that describes the deformation of a body under stress is known as strain. Strain is given as a fractional change in either length, volume, or geometry under tensile, volume (also known as bulk), or shear stress, respectively, and is a dimensionless quantity. The strain experienced by a body under tensile or compressive stress is called tensile or compressive strain, respectively. In contrast, the strain experienced under bulk stress and shear stress is known as volume and shear...
5.0K
Dynamic Modulus of Elasticity of Concrete01:16

Dynamic Modulus of Elasticity of Concrete

The dynamic modulus of elasticity assesses how a concrete structure deforms under impact or dynamic loads. It is typically higher than the static modulus of elasticity, measured under slow, steady loading conditions.
The sonic test is a common method to determine the dynamic modulus. In this test, a concrete beam, sized either 6 x 6 x 30 inches or 4 x 4 x 20 inches, is clamped at its center. Vibrations are initiated at one end of the beam by an electromagnetic exciter unit powered by a...
647
Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity01:15

Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity

Deformation occurs in axial and transverse directions when an axial load is applied to a slender bar. This deformation impacts the cubic element within the bar, transforming it into either a rectangular parallelepiped or a rhombus, contingent on its orientation. This transformation process induces shearing strain. Axial loading elicits both shearing and normal strains. Applying an axial load instigates equal normal and shearing stresses on elements oriented at a 45° angle to the load axis.
385
Hooke's Law01:26

Hooke's Law

Hooke's law, a pivotal principle in material science, establishes that the strain a material undergoes is directly proportional to the applied stress, defined by a factor called the modulus of elasticity or Young's modulus.
834
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
278