Characterization of underutilized root starches from eight varieties of ramie (Boehmeria nivea) grown in China

Ramie root is an underutilized starch source. In this study, eight ramie varieties were investigated for starch properties. Starch content ranged from 18.6% to 50.1% in dry root. Starches from different varieties showed similar morphology including ellipsoidal, spherical and truncated granules with size D[4,3] from 10.1 to 14.1 μm. Starch had amylose content from 20.8% to 28.5%. All ramie varieties had B-type starches with relative crystallinity from 24.8% to 27.1%, ordered degree from 0.724 to 0.897 and lamellar thickness from 9.1 to 9.6 nm. Starches had gelatinization peak temperature from 70.5 to 73.8 °C and enthalpy from 14.9 to 15.8 J/g. Starches had swelling power and water solubility from 27.9 to 31.9 g/g and from 11.7% to 15.5%, respectively, at 95 °C, and exhibited different pasting properties with breakdown viscosity from 36 to 377 mPa s and setback viscosities from 1295 to 1863 mPa s. Starch pastes exhibited pseudoplastic behavior and different rheological properties. Native, gelatinized and retrograded starches had resistant starch from 81.7% to 83.9%, from 1.7% to 5.1% and from 5.6% to 13.3%, respectively. The eight varieties were divided into 3 groups according to starch properties. This study is helpful for selecting suitable ramie variety as starch source.