[Biocompatibility of extracellular matrix hydrogel with human iPSCs differentiated cardiomyocytes]

Objective: To observe the biocompatibility of porcine omental derived extracellular matrix (ECM) hydrogel with human induced pluripotent stem cell-derived cardiomyocytes (hiPSC-CMs) and the feasibility of ECM hydrogel as a delivery vector of cell transplantation. Methods: A series of chemical, physical and enzymatic methods were applied to acellularize the porcine omentum. Subsequently, the extracted ECM was prepared into thermosensitive hydrogel. The biochemical composition of the hydrogel was identified by histological staining. The microstructure was observed by scanning electron microscopy. The hydrogel was then injected into the myocardium of mice to observe its in situ gelation ability. Differentiation of human induced pluripotent stem cells into cardiomyocytes was achieved by small molecule induction, and then the obtained hiPSC-CMs were cultured. hiPSC-CMs cultured onto the prepared hydrogel were defined as the hydrogel group, while conventionally cultured hiPSC-CMs were defined as the control group. Cardiomyocyte viability and growth patterns were detected using live/dead staining, CCK-8 and phalloidin staining. Immunofluorescence staining and Western blot of cardiomyocytes were used to determine the survival and phenotypic maintenance markers of cardiomyocytes in materials. Results: The results of HE staining, oil red O staining and DAPI fluorescence staining showed that there was no significant cell debris, nucleus and lipid residue in the prepared ECM hydrogel. The Sirius red staining and Alcian blue staining showed that the hydrogel retained collagen and glycolaminoglycan, which were the main components of ECM. The prepared hydrogel behaves as a viscous liquid at 4 ℃ and as a gel state at 37 ℃. Scanning electron microscope results showed that the microstructure of the hydrogel was composed of irregular fibers and pores of different sizes. Under the guidance of ultrasound, the prepared ECM hydrogel could be successfully injected into the myocardium of mice. Immediately after the injection, the hyperechoic signal could be observed under ultrasound, suggesting that the hydrogel remained in the myocardium. HE staining of myocardial tissue evidenced that there was lump of gel in the injection area. The differentiated hiPSC-CMs were co-cultured with the prepared ECM hydrogel, and the results of live/dead staining showed that most of the hiPSC-CMs in the hydrogel group and the control group were alive, dead cells were scanty. The results of CCK-8 test showed that the absorbance values of the two groups were similar (P>0.05). The results of phalloidin staining showed that hiPSC-CMs could extend normally when co-cultured with ECM hydrogel. The cell morphology of the hydrogel group was similar with that of the control group, and there was no statistically significant difference in the F-actin coverage area per cell between the two groups (P>0.05). Immunofluorescence staining of cardiomyocyte markers showed that there was no significant difference in the coverage area of α-actinin and connexin-43 (Cx-43) per field between the hydrogel group and the control group (both P>0.05), the quantitative results of DAPI staining showed that there was no statistically significant difference in the number of cells between the two groups (P>0.05). Meanwhile, the results of Western blot showed that the expression levels of α-actinin and Cx-43 in cardiomyocytes in the hydrogel group were similar as those in the control group (both P>0.05). Conclusions: These results show that preparation of the ECM hydrogel from porcine omentum is successful. The hydrogel has good biocompatibility and no obvious cytotoxicity. Besides, the hydrogel can support the survival of hiPSC-CMs in vitro and maintain its phenotype. These properties make it a promising injectable cardiac tissue engineering material.