Formation of PbCl₂-type AHF (A = Ca, Sr, Ba) with partial anion order at high pressure

The high-pressure structures of alkaline earth metal hydride-fluorides (AHFs) (A = Ca, Sr, Ba) were investigated up to 8 GPa. While AHF adopts the fluorite-type structure (Fm3[combining macron]m) at ambient pressure without anion ordering, the PbCl2-type (cotunnite-type) structure (Pnma) is formed by pressurization, with a declining trend of critical pressure as the ionic radius of the A2+ cation increases. In contrast to PbCl2-type LaHO and LaOF whose anions are fully ordered, the H-/F- anions in the high-pressure polymorph of SrHF and BaHF are partially ordered, with a preferential occupation of H- at the square-pyramidal site (vs. tetrahedral site). First-principles calculations partially support the preferential anion occupation and suggest occupation switching at higher pressure. These results provide a strategy for controlling the anion ordering and local structure in mixed-anion compounds.