A Sulfhydryl Azobenzene-Modified Polyaniline/Silver Electrode and Its Photoswitching Electrochemical Performance

In this work, a sulfhydryl-functionalized azobenzene derivative (Azo) was synthesized and polyaniline/silver was modified (PANI/Ag) to make a nanocomposite (PANI/Ag/Azo). A series of characterization techniques like¹HNMR, UV-vis absorption spectra, Raman spectra, FT-IR, XRD, SEM, TEM, and TGA was employed to study Azo, PANI/Ag, and PANI/Ag/Azo. Electrochemical properties were measured by cyclic voltammetry (CV) and galvanostatic charging/discharging (GCD). CV showed that UV and blue light had hardly any effect on PANI/Ag. However, with the prolonged exposure time of UV light, the maximum CV current density of PANI/Ag/Azo rose from 1.24 to 2.72 A g^-1. Then, after 20 min of blue light irradiation, the maximum current density gradually recovered (from 2.72 to 1.26 A g^-1). The GCD also obtained similar results. After formula calculation, the specific capacitance of PANI/Ag/Azo also presented a reversible trend under the alternating irradiation of UV light and blue light. All the results show that PANI/Ag/Azo has a good photoelectric response, and its electrochemical performance can be reversibly adjusted by light. This result provides a new design idea for developing electrode materials with real-time electrochemical properties.