Effects of ZnMgO Electron Transport Layer on the Performance of InP-Based Inverted Quantum Dot Light-Emitting Diodes

An environment-friendly inverted indium phosphide red quantum dot light-emitting diode (InP QLED) was fabricated using Mg-doped zinc oxide (ZnMgO) as the electron transport layer (ETL). The effects of ZnMgO ETL on the performance of InP QLED were investigated. X-ray diffraction (XRD) analysis indicated that ZnMgO film has an amorphous structure, which is similar to zinc oxide (ZnO) film. Comparison of morphology between ZnO film and ZnMgO film demonstrated that Mg-doped ZnO film remains a high-quality surface (root mean square roughness: 0.86 nm) as smooth as ZnO film. The optical band gap and ultraviolet photoelectron spectroscopy (UPS) analysis revealed that the conduction band of ZnO shifts to a more matched position with InP quantum dot after Mg-doping, resulting in the decrease in turn-on voltage from 2.51 to 2.32 V. In addition, the ratio of irradiation recombination of QLED increases from 7% to 25% using ZnMgO ETL, which can be attributed to reduction in trap state by introducing Mg ions into ZnO lattices. As a result, ZnMgO is a promising material to enhance the performance of inverted InP QLED. This work suggests that ZnMgO has the potential to improve the performance of QLED, which consists of the ITO/ETL/InP QDs/TCTA/MoO₃/Al, and Mg-doping strategy is an efficient route to directionally regulate ZnO conduction bands.