Effects of pullulan on the biomechanical and anti-collapse properties of dicalcium phosphate dihydrate bone cement

In this work, a modified dicalcium phosphate dihydrate (DCPD) bone cement with unique biodegradable ability in a calcium phosphate cement system was prepared by the hydration reaction of monocalcium phosphate monohydrate and calcium oxide and integration with pullulan (Pul), a non-toxic, biocompatible, viscous, and water-soluble polysaccharide that has been successfully used to improve defects in DCPD bone cement, especially its rapid solidification, fragile mechanical properties, and easy collapse. The effect of different contents of Pul on the structure and properties of DCPD were also studied in detail. The modified cement was characterised by X-ray diffraction, Fourier-transform infrared spectroscopy, scanning electron microscopy, ultraviolet-visible absorption, X-ray photoelectron spectroscopy analysis, and rheological property measurements. The results indicated that Pul promoted the hydration formation of DCPD, and interface bonding occurred between Pul and DCPD. With increasing content of Pul, the setting time of the DCPD bone cement increased from 2.6 min to 42.3 min, the compressive strength increased from 0 MPa to 20.4 MPa, and the anti-collapse ability also improved owing to the strong interface bonding, implying that the DCPD bone cement improved by Pul has better potential for application in the field of non-loading bone regenerative medicine compared to unmodified DCPD bone cement.