Development of a low elastic modulus and antibacterial Ti-13Nb-13Zr-5Cu titanium alloy by microstructure controlling
Anqi Shi1, Diangeng Cai1, Jiali Hu1
1Key Lab. for Anisotropy and Texture of Materials, Education Ministry of China, School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China.
Abstract:
In order to prepare a titanium with a low elastic modulus and good antibacterial property to meet the requirements as a biomedical material, Ti-13Nb-13Zr-5Cu (TNZ-5Cu) alloy was prepared by high vacuum consume electric arc melting furnace and then subjected to a solution treatment at 950 °C followed by a short-term aging treatment at 600 °C, for 15 min, 30 min, 1 h and 2 h, respectively. The microstructure, mechanical property, antibacterial property and biocompatibility of TNZ-5Cu were investigated in detail. The research results have shown that the solid solution treated alloy was mainly composed of β-phase and α″-phase, while the aged alloys of β-phase, α″-phase, α-phase and Ti2Cu. Compared with Ti-13Nb-13Zr alloy (65 GPa) and Ti-6Al-4 V alloy (111 GPa), the elastic modulus of TNZ-5Cu alloy after solution treatment was about 72 GPa and increased with the aging treatment up to 85 GPa, and the hardness was maintained at a higher level than that of Ti-13Nb-13Zr alloys (288 HV). The bacteria plate count results showed that the antibacterial ability of TNZ-5Cu alloy increased with the extension of the aging duration from <60% at 15-30 min to >90% at 1-2 h. Cell experiments showed that all TNZ-5Cu alloy had good cell compatibility. The low modulus and the antibacterial property could provide potential to avoid stress shield and device-related inflection in the clinical application.