The role of fretting-frequency on the damage modes of THR modular junction: In-vitro study

According to the National Center for Health Statistics, currently, more than 250,000 total hip replacements annually in the US alone, with an estimated increase to 500,000 by the year 2030. The usage of tapered junctions between the femoral neck and head gives the surgeon flexibility in implant assembly. However, these modular junctions are subjected to micro-motion that may cause chemical and fretting-corrosion at the modular junction. Therefore, it is imperative to study these forces to mitigate their effects. The current study aims to understand the effects of fretting-corrosion as a function of fretting frequencies caused by common physical activities in an in-vitro model of hip modular junctions. The fretting system has a tribological contact condition of flat-on-flat, mounted to a load frame. CoCrMo pins were polished and immersed in a synovial fluid-like electrolyte solution (Bovine calf serum 30 g/l). Electrochemical measurements were made using a potentiostat. Samples then undergo 3600 cycles at 50 μm (to simulate gross slips), with a horizontal load at 200 N, and a frequency of 0.5 Hz, 0.7 Hz, 1 Hz, and 1.5 Hz to simulate Sit Down-Stand Up, Stair Climb, Walking, and Jogging, respectively. Worn surfaces were then examined under optical and scanning electron microscopy. The evolution of free potential as a function of time for tested frequencies shows the initial potential drop and stabilized trend in the potential evolution. The sample group at a higher frequency displays a higher tendency of corrosion than a lower frequency; however, the dissipation energy decreases as a function of fretting frequency. Both electrochemical and mechanical responses correlate to the variation in the fretting frequencies. Organometallic complexes were found on the surfaces of the samples that were subjected to a slower frequency of fretting, whereas mechanical grooving was noticed on samples with a faster frequency. Hence, these preliminary studies suggest that implant failure rates may be altered based on fretting-frequencies induced by physical activity. Further studies will be required to verify the findings and explore the potential role of fretting frequency in the damage modes of the modular junction.