Formulation of inherently antimicrobial magnesium oxychloride cement and the effect of supplementation with silver...

The growing threat of bacterial resistance to antibiotics is driving an increasing need for new antimicrobial strategies. This work demonstrates the potential of magnesium oxychloride cements (MOC) to be used as inorganic antimicrobial biomaterials for bone augmentation. An injectable formulation was identified at a powder to liquid ratio of 1.4 g mL^-1, with an initial setting time below 30 mins and compressive strength of 35 ± 9 MPa. Supplementation with Ag₃PO₄ to enhance the antimicrobial efficacy of MOC was explored, and shown via real time X-ray diffraction to retard the formation of hydrated oxychloride phases by up to 30%. The antimicrobial efficacy of MOC was demonstrated in vitro against Staphylococcus aureus and Pseudomonas aeruginosa, forming zones of inhibition and significantly reducing viability in broth culture. Enhanced efficacy was seen for silver doped formulations, with complete eradication of detectable viable colonies within 3 h, whilst retaining the cytocompatibility of MOC. Investigating the antimicrobial mode of action revealed that Mg and Ag release and elevated pH contributed to MOC efficacy. Sustained silver release was demonstrated over 14 days, suggesting the Ag₃PO₄ modified formulation offers two mechanisms of infection treatment, combining the inherent antimicrobial properties of MOC with controlled release of inorganic antimicrobials.