Boronate affinity imprinted hydrogel sorbent from biphasic synergistic high internal phase emulsions reactor for...

The dynamic coexistence of heterostructures is crucial for the synergistic function of molecularly imprinted polymers (MIPs) derived from high internal phase emulsions (HIPEs). In this work, hydrophilic boronate affinity imprinted hydrogel sorbents (H-UIO-66-NH₂-IHIPEs) were prepared by biphasic synergistic HIPEs droplet reactors filled with reactive microencapsulation system, and used to capture and separate cis-diol containing luteolin (LTL) from complex extraction samples with high selectivity. As the main solid emulsifier, UiO-66-NH₂, prototype zirconium-based metal-organic frameworks (MOFs) greatly improves the mechanical performance of the hydrogel, whilst preventing overuse of surfactants. Space-confined formation of imprinted sites in the external phase is realized in the presence of hydrophilic acrylamide phenylboric acid monomer (H-BA), which endows the specific affinity with pH responsiveness to LTL. In addition, the filled microinclusion compound containing elastic monomer octadecyl methacrylate (SMA) and functional monomer glycidyl methacrylate (GMA) simultaneously added interfacial cross-linking reaction to provide stable pore volume and pore shape. Combined with these excellent properties, H-UIO-66-NH₂-IHIPEs showed fast capture kinetics (75 min) and large uptake amount (39.77 mg g^-1) at 298 K, and confirmed the existence of a uniform chemisorption monolayer. Moreover, excellent recyclability of 6.24% loss in adsorption amount after five adsorption-desorption cycles was observed. Finally, the LTL content of the purified product (about 97.38%) was higher than that of the crude extract (about 85.0%). This study sheds a new light for the design of novel imprinted hydrogel sorbents combined with binary synergistic components.