Physicochemical impact of cellulose nanocrystal on oxidation of starch and starch based composite films

A cellulose nanocrystal based oxidation system is developed for oxidizing starch in the presence of NaClO, and provides an alternative and green method to improve the oxidizing degree of oxidized starch. The underlying mechanism for the oxidation was studied with confocal laser scanning microscopy. It was found that cellulose nanocrystal would penetrate into the starch microparticles and contribute to oxidation. The function of cellulose nanocrystal on the physicochemical properties of oxidized starch was investigated. With the incorporation of the oxidized starch into starch/polyvinyl alcohol/glyceryl composite films, the mechanical property and transparency of the films improved substantially. The highest oxidation level of starch was attained at 0.5 wt% cellulose nanocrystal dosage and the carboxylate content was 1.10%, the composite film showed the maximum transparency of 0.66 and highest contact angle of 102.0°. Meanwhile, the best film was obtained with oxidized starch containing 1.0 wt% cellulose nanocrystal. Compared to native starch and TEMPO-oxidated starch, the cellulose nanocrystal-based oxidized starch improved the hydrophobicity of film more substanially. In conclusion, cellulose nanocrystal acts as prooxidant and reforcing agent in this starch-based composite film, which makes them promising materials in the preparation of novel composite materials.