Engineering Quick- and Long-acting Naloxone Delivery Systems for Treating Opioid Overdose

Opioids have been the main factor for drug overdose deaths in the United States. Current naloxone delivery systems are effective in mitigating the opioid effects only for hours. Naloxone-loaded poly(lactide-co-glycolide) (PLGA) microparticles were prepared as quick- and long-acting naloxone delivery systems to extend the naloxone effect as an opioid antidote.

The naloxone-PLGA microparticles were made using an emulsification solvent extraction approach with different formulation and processing parameters. Two PLGA polymers with the lactide:glycolide (L:G) ratios of 50:50 and 75:25 were used, and the drug loading was varied from 21% to 51%. Two different microparticles of different sizes with the average diameters of 23 μm and 50 μm were produced using two homogenization-sieving conditions. All the microparticles were critically characterized, and three of them were evaluated with β-arrestin recruitment assays.

The naloxone encapsulation efficiency (EE) was in the range of 70-85%. The EE was enhanced when the theoretical naloxone loading was increased from 30% to 60%, the L:G ratio was changed from 50:50 to 75:25, and the average size of the particles was reduced from 50 μm to 23 μm. The in vitro naloxone release duration ranged from 4 to 35 days. Reducing the average size of the microparticles from 50 μm to 23 μm helped eliminate the lag phase and obtain the steady-state drug release profile. The cellular pharmacodynamics of three selected formulations were evaluated by applying DAMGO, a synthetic opioid peptide agonist to a μ-opioid receptor, to recruit β-arrestin 2.

Naloxone released from the three selected formulations could inhibit DAMGO-induced β-arrestin 2 recruitment. This indicates that the proposed naloxone delivery system is adequate for opioid reversal during the naloxone release duration.