Simultaneously enhancing redox kinetics and inhibiting the polysulfide shuttle effect using MOF-derived CoSe hollow...

Lithium-sulfur (Li-S) batteries generally suffer from a serious "shuttle effect" during the charging/discharging process, resulting in the loss of active components and sluggish redox reaction kinetics that hinder the cycle life and rate performance of the battery. To address this, CoSe/C hollow structures (CoSe/C HSs) were prepared via a simple hydrothermal strategy and used as a sulfur host for Li-S batteries. The battery with CoSe/C HSs exhibited a high initial specific discharge capacity of 1405 mA h g-1 with a coulombic efficiency of 99.8% at 0.1C. Additionally, S@CoSe/C HS cathodes with a high sulfur loading of 5.1 mg cm-2 delivered a considerable specific discharge capacity of 1256.1 mA h g-1 and maintained a high capacity of 1120 mA h g-1 after 100 cycles with a capacity decay rate of 0.11% per cycle at 0.1C. The unique raspberry-like structure of CoSe/C HSs prevents polysulfides from escaping the cathode host via both physical containment and the formation of Co-S and Se-Li chemical bonds, and it also enhances the polysulfide redox kinetics. Furthermore, the peculiar raspberry-like structure can withstand volume changes during charging/discharging to better protect the cathode.