Interfacial Engineering of Cu₂O Passivating Contact for Efficient Crystalline Silicon Solar Cells with an Al₂O₃...

Passivating contacts that simultaneously promote carrier selectivity and suppress surface recombination are considered as a promising trend in the crystalline silicon (c-Si) photovoltaic industry. In this work, efficient p-type c-Si (p-Si) solar cells with cuprous oxide (Cu₂O) hole-selective contacts are demonstrated. The direct p-Si/Cu₂O contact leads to a substoichiometric SiO interlayer and diffusion of Cu into the silicon substrate, which would generate a deep-level impurity behaving as carrier recombination centers. An Al₂O₃ layer is subsequently employed at the p-Si/Cu₂O interface, which not only serves as a passivating and tunneling layer but also suppresses the redox reaction and Cu diffusion at the Si/Cu₂O interface. In conjunction with the high work function of Au and the superior optical property of Ag, a power conversion efficiency up to 19.71% is achieved with a p-Si/Al₂O₃/Cu₂O/Au/Ag rear contact. This work provides a strategy for reducing interfacial defects and lowering energy barrier height in passivating contact solar cells.