Deep-Level Transient Spectroscopy for Effective Passivator Selection in Perovskite Solar Cells to Attain High
Xiaodong Ren1, Bobo Zhang1, Lu Zhang1
1Key Laboratory of Applied Surface and Colloid Chemistry, Ministry of Education, Shaanxi Key Laboratory for Advanced Energy Devices, Shaanxi Engineering Lab for Advanced Energy Technology, Institute for Advanced Energy Materials, School of Materials Science and Engineering, Shaanxi Normal University, Xi'an, 710119, P. R. China.
Abstract:
Most studies choose passivators essentially in a trial-and-error fashion in an attempt to attain high efficiency in perovskite solar cells (PSCs). Using deep-level transient spectroscopy (DLTS) measurements, the type of defects in perovskite films was determined to guide the passivator selection for PSCs. Three kinds of positively charged defects were found in the target PSC system. Fluorinated phenylethylamine hydroiodide (FPEAI) was chosen to passivate the surface defects due to the electronegativity and hydrophobicity of fluorine. Due to the decreased surface roughness, increased hydrophobicity, lowered defect density, and improved carrier dynamics as observed by ultrafast transient absorption spectroscopy (TAS), a PSC with meta-F-PEAI had the best efficiency over 23 % with open-circuit voltage of 1.155 V and fill factor of 80.15 %. In addition, the long-term stability of the PSC was significantly improved. The present work provides a new means to select the best passivator for different types of defects.
More Related Videos
11:38Influence of Hybrid Perovskite Fabrication Methods on Film Formation, Electronic Structure, and Solar Cell Performance
Published on: February 27, 2017
06:49In situ Grazing Incidence Small Angle X-ray Scattering on Roll-To-Roll Coating of Organic Solar Cells with Laboratory X-ray Instrumentation
Published on: March 2, 2021