Emission tuning of highly efficient quaternary Ag-Cu-Ga-Se/ZnSe quantum dots for white light-emitting diodes

With the blooming development of zero-dimensional nanomaterials, I-III-VI alloying quantum dots (QDs) with outstanding photoelectrical properties have emerged to attract much attention as promising environmentally-friendly substitutions for conventional binary Cd-based QDs. In this work, a facile one-pot method was introduced to synthesize unreported quaternary Ag-Cu-Ga-Se/ZnSe (ACGSe/ZnSe) QDs. A relatively high photoluminescence quantum yield (PL QY) of 71.9% and a tunable emission from 510 to 620 nm were successfully achieved. We explored the roles of alloying compositions in ACGSe/ZnSe QDs, inferring that increased Ag proportion would not only lower the V_defect level which leads to the blue shift of emission, but also slow the ZnSe shelling process owing to the larger lattice distortion. At last, the white light-emitting diodes (WLEDs) were fabricated with ACGSe/ZnSe QDs as the conversion layer, indicating that the as-prepared QDs are a promising candidate for further applications.