Trimetallic synergy in dendritic intermetallic PtSnBi nanoalloys for promoting electrocatalytic alcohol oxidation

Developing effective and robust novel electrocatalysts for direct alcohol fuel cells has been gaining much attention. However, the widely used Pt catalyst suffers from limitations including the sluggish kinetics, severe CO poisoning, and catalyst lost caused by aggregation and Ostwald ripening during alcohol oxidation reaction. Herein, dendritic intermetallic PtSnBi nanoalloys were synthesized via a facile hydrothermal approach with high electrocatalytic performance and enhanced CO resistance for methanol oxidation reaction (MOR) and ethanol oxidation reaction (EOR) owing to the synergism of the chosen three elements and unique three-dimensional morphology. Specifically, the PtSnBi nanoalloys display 4.6 and 6.7 times higher of mass activity (7.02 A mg^-1_Pt) and specific activity (16.65 mA cm^-2) toward MOR than those of commercial Pt/C, respectively. The mass activity of PtSnBi nanoalloys still retains 75.7% of the initial value after 800 cycles of stability test, superior to Pt/C (38.0%). The dual-functional effect of Sn, optimized electronic structure by the ligand effect, and unique atomic arrangement are responsible for the enhanced MOR activity and stability of PtSnBi nanoalloys. Furthermore, the PtSnBi nanoalloys with highlighted anti-CO poisoning capacity also improve the electrocatalytic performance toward EOR, indicating their great promise as broad energy electrocatalysts.