Removal of levofloxacin through adsorption and peroxymonosulfate activation using carbothermal reduction synthesized...

Nano zero-valent iron (nZVI) is widely used for decontamination. The main issues associated with nZVI are agglomeration and oxidation in the long term. In this study, the carbothermal reduction of cotton fiber was conducted for the synthesis of nZVI supported on cotton carbon fiber (nZVI/CF) to address the agglomeration and oxidation of nZVI. Synergistic adsorption and peroxymonosulfate (PMS) activation using nZVI/CF for removing levofloxacin (LEV) are reported herein. The nZVI concentration and morphology were conveniently adjusted by soaking cotton fiber in ferric nitrate solutions of various Fe³⁺ concentrations. The carbothermal reduction of the cotton fiber at 900 °C contributed to the reduction of Fe³⁺ into nZVI. A nZVI/CF-900-0.3 system was obtained through the carbothermal reduction of cotton fiber soaked in 0.3 M ferric nitrate. Favorable adsorption of nZVI/CF-900-0.3 to LEV facilitated LEV degradation under PMS activation. Approximately 93.83% of LEV (C₀ = 20 ppm) was removed within 60 min with 0.2 g/L of the catalyst and 1 mM PMS. It was preferable to use nZVI + CF-900 to activate PMS for degrading LEV, thus confirming the favorable effect of LEV adsorption on further degradation. The nZVI/CF-900-0.3 exhibited excellent long-term stability given that it was able to activate PMS after it was stored for 6 months. ·SO₄^- played an important role in LEV degradation in the presence of PMS.