Large Perpendicular Magnetic Anisotropy in Ta/CoFeB/MgO on Full-Coverage Monolayer MoS2 and First-Principles Study of
Ziqi Zhou1,2, Paul Marcon3, Xavier Devaux2
1State Key Laboratory of Superlattices and Microstructures, Institute of Semiconductors, Chinese Academy of Sciences & Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing 100083, China.
Abstract:
A perpendicularly magnetized spin injector with a high Curie temperature is a prerequisite for developing spin optoelectronic devices on two-dimensional (2D) materials working at room temperature (RT) with zero applied magnetic field. Here, we report the growth of Ta/CoFeB/MgO structures with large perpendicular magnetic anisotropy (PMA) on full-coverage monolayer (ML) molybdenum disulfide (MoS2). A large perpendicular interface anisotropy energy of 0.975 mJ/m2 has been obtained at the CoFeB/MgO interface, comparable to that observed in magnetic tunnel junction systems. It is found that the insertion of MgO between the ferromagnetic (FM) metal and the 2D material can effectively prevent the diffusion of the FM atoms into the 2D material. Moreover, the MoS2 ML favors a MgO(001) texture and plays a critical role in establishing the large PMA. First-principles calculations on a similar Fe/MgO/MoS2 structure reveal that the MgO thickness can modify the MoS2 band structure, from a direct band gap with 3ML-MgO to an indirect band gap with 7 ML-MgO. The proximity effect induced by Fe results in splitting of 10 meV in the valence band at the Γ point for the 3ML-MgO structure, while it is negligible for the 7 ML-MgO structure. These results pave the way to develop RT spin optoelectronic devices based on 2D transition-metal dichalcogenide materials.
More Related Videos
Related Concept Videos
01:31Ferromagnetism
02:42Valence Bond Theory
01:31Magnetic Susceptibility and Permeability
When diamagnetic materials are placed under an external magnetic field, the moments opposite to the field are induced. Hence, the susceptibility for diamagnets has a minimal negative value of 10-5–10-6. Since...
02:40MO Theory and Covalent Bonding
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human...
01:26Diamagnetism
Diamagnetism was discovered by Anton Brugmans in 1778 when he observed that bismuth gets repelled by magnetic fields, thus theorizing that diamagnets get repelled by magnets....