Ambient Air Temperature Assisted Crystallization for Inorganic CsPbI₂Br Perovskite Solar Cells

Inorganic cesium lead halide perovskites, as alternative light absorbers for organic-inorganic hybrid perovskite solar cells, have attracted more and more attention due to their superb thermal stability for photovoltaic applications. However, the humid air instability of CsPbI₂Br perovskite solar cells (PSCs) hinders their further development. The optoelectronic properties of CsPbI₂Br films are closely related to the quality of films, so preparing high-quality perovskite films is crucial for fabricating high-performance PSCs. For the first time, we demonstrate that the regulation of ambient temperature of the dry air in the glovebox is able to control the growth of CsPbI₂Br crystals and further optimize the morphology of CsPbI₂Br film. Through controlling the ambient air temperature assisted crystallization, high-quality CsPbI₂Br films are obtained, with advantages such as larger crystalline grains, negligible crystal boundaries, absence of pinholes, lower defect density, and faster carrier mobility. Accordingly, the PSCs based on as-prepared CsPbI₂Br film achieve a power conversion efficiency of 15.5% (the maximum stabilized power output of 15.02%). Moreover, the optimized CsPbI₂Br films show excellent robustness against moisture and oxygen and maintain the photovoltaic dark phase after 3 h aging in an air atmosphere at room temperature and 35% relative humidity (R.H.). In comparison, the pristine films are completely converted to the yellow phase in 1.5 h.