Chemical Modification of Banana Trunk Fibers for the Production of Green Composites

Natural fibers have proven to be excellent reinforcing agents in composite materials. However, a critical disadvantage of natural fibers is their hydrophilic nature. In this study, banana trunk fibers were mechanically damaged using a high-speed blender, and the resulting fibers (MDBTF) were treated with (i) stearic acid (SAMDBTF) and (ii) calcium carbonate coated with 5% (wt/wt) stearic acid (SACCMDBTF). The moisture sorption, oil sorption and thermal properties of the fibers were determined. The morphology, roughness and the functional groups present were also investigated. Study data of the present study indicate that SACCMDBTF exhibited a faster oil sorption capacity than SAMDBTF. Fast uptake of the oil occurred during the first 5 min, whereby the quantity of oil sorbed in SAMDBTF and SACCMDBTF was 5.5 and 15.0 g oil g^-1 fiber, respectively. The results of a used engine oil uptake study revealed that SAMDBTF and SACCMDBTF sorbed 9.5 and 18.3 g/g-1 fiber, respectively, at equilibrium. The obtained results suggest that the mechanically damaged process improved the thermal stability of the fibers. This work reveals that the inclusion of stearic-acid-coated calcium carbonate into the interstices of MDBTF yields is environmentally safe for green hydrophobic composites. SACCMDBTF are used as efficient adsorbents for the removal of spilled oil on aqueous media.