Controllable synthesis of ZIF-derived NiCo3-O4 nanotube array hierarchical structures based on self-assembly for
Bei Xue1, Yao Guo2, Zhaofeng Huang3
1Department of Materials Physics, School of Science, Xi'an University of Posts and Telecommunications, Xi'an 710121, China. xuebei312@outlook.com xuebei@xupt.edu.cn.
Abstract:
In this study, a novel NixCo3-xO4 nanotube array hierarchical structure derived from zeolitic imidazolate frameworks (ZIFs) is grown on Ni foam (NixCo3-xO4 NAHS/Ni foam) using the template-assisted and self-assembly approach for a high-performance hybrid energy storage device in alkaline solution. The material characteristics of the resultant samples were characterized by XPS, XRD, ICP, SEM, TEM and BET. Due to the unique hollow structure with a large specific surface area and the exposure of large active sites originating from ZIFs, the optimal NixCo3-xO4 NAHS/Ni foam exhibits substantially enhanced electrochemical properties. The NixCo3-xO4 NAHS/Ni foam directly acts as an electrode, which provides an excellent specific capacity of 290.48 mA h g-1 at 1 A g-1. Subsequently, the corresponding hybrid alkaline batteries that consist of NixCo3-xO4 NAHS/Ni foam and carbon materials display a highly satisfactory specific capacity of 54.94 mA h g-1 at 1 A g-1, a satisfactory long-term stability of 85.47% after 2000 cycles, a maximum energy density of 43.95 W h kg-1 and a power density of 8000 W kg-1. This work combines the design of the electronic structure with the optimization of composition, and provides a reference for the application of hybrid rechargeable alkaline batteries (RABs).