Bonding Performance of Self-etching Adhesives to Bur-cut Dentin with Active Application Mode

This study evaluated whether active application of self-etching adhesives would influence their microtensile bond strength (µTBS) to dentin cut with burs of different grit sizes.

Eighty-four human premolars were divided into 12 groups according to 1) two dentin surface preparations with either superfine- or regular-grit diamond burs; 2) three adhesives - Clearfil SE Bond 2 (SE2), Scotchbond Universal (SBU, 3M Oral Care) and G-Premio Bond (GPB, GC); and 3) two application modes of each adhesive (active or passive). Six bonded teeth per group were sectioned into sticks for µTBS testing. Statistical analyses were performed using 3-way ANOVA followed by Duncan's test (p < 0.05). Additional teeth were prepared to observe the interaction between the dentin smear layer obtained from each bur with adhesives under different application modes using transmission electron microscopy (TEM).

Active application significantly increased the dentin bond strength of SE2, irrespective of the kind of bur used (p < 0.05). The highest bond strength of SBU was observed when bonded to superfine-grit diamond bur-cut dentin with the active application. There was, however, no influence of the tested factors on GPB group (p > 0.05). TEM observation showed that active application promoted dentin smear layer dissolution in all adhesive groups.

Bond strengths of self-etching adhesives to dentin are influenced by bur-cut smear layers and mainly by application mode of adhesive materials. Active application improves µTBS of self-etching adhesives by enhancing smear layer modification and resin penetration into bur-cut dentin.