Effect of Nano-Magnesium Oxide on the Expansion Performance and Hydration Process of Cement-Based Materials

Many scholars are concerned about the effect of nano-MgO as an expansion agent on the performance of cement-based materials at an early age, but over a long period less attention is paid to expansion stability and mechanical properties. This article examines the influence of nano-MgO on the long-term consistency, fluidity, expansion stability, hydration, and mechanical properties of 30% fly ash cement-based materials and improves research into nano-MgO as an expansion agent. Expansion performance, flexural and compressive strength, and stability after boiling and autoclave treatment were tested for specimens mixed with a 2, 4, 6, 8 and 10% cementitious material mass of nano-MgO. X-ray diffraction (XRD) and scanning electronic microscopy (SEM) were employed to study their hydration process and microstructure. The results showed that nano-MgO had an obvious effect on the consistency, fluidity and expansion performance of cement paste. After curing in water for 365 days and autoclaving thereafter, the hydration of nano-MgO was relatively complete. The volumetric expansion pressure of the magnesium hydroxide (Mg(OH)₂) crystals and the crystallization pressure generated after their continuous precipitation were the main reasons for the expansion of the slurry. Nano-MgO improved the microstructure of cement paste and significantly enhanced its long-term flexural strength and compressive strength. When the content of nano-MgO was less than 10%, the cement with 30% fly ash had good long-term stability with the potential to compensate for the shrinkage of large-volume concrete.