Study on Properties of Bone Glue/Polyurethane Composite Modified Asphalt and Its Mixture

Composite modification technology is widely used in the materials field. To enhance the property of polyurethane modified asphalt and realize its application in road engineering, the bone glue/polyurethane composite modified asphalt (CMA) was prepared using bone glue, polyurethane, and neat asphalt in this research. The bone glue content ranges 5-10%, that of the polyurethane is 1-5%. The relationship between the modifier's content and the conventional properties and rheological properties of CMA was revealed by response surface methodology (RSM). The CMA performance was further verified under the optimal content of the bone glue and polyurethane. The differences of properties of styrene-butadienestyrene (SBS) modified asphalt mixture, neat asphalt mixture, and bone glue/polyurethane CMA mixture were compared and analyzed by using the pavement performance test. The results showed that the CMA's conventional properties and rheological properties are improved. The optimal bone glue content and polyurethane content determined by RSM are 6.848% and 2.759%, respectively. The low-temperature crack resistance and water stability of the CMA mixture are enhanced, better than neat asphalt mixture and SBS modified asphalt mixture. The CMA mixture's dynamic stability is 85% of SBS modified asphalt mixture, but it is 2.4 times of neat asphalt mixture. The result indicated that the bone glue/polyurethane CMA mixture still has certain advantages of high-temperature stability. In this research, the composite modification of bone glue and polyurethane can significantly enhance the characteristic of asphalt and asphalt mixture and provide a new method for applying and promoting polyurethane modified asphalt in road engineering.