Comparison of translucency and opalescence among different dental monolithic ceramics
Mohammadjavad Shirani1, Omid Savabi2, Ramin Mosharraf3
1Assistant Professor, Department of Prosthodontics, School of Dentistry, Lorestan University of Medical Sciences, Khorramabad, Iran.
Statement Of Problem:
Monolithic ceramic restorations designed by computer-aided design and computer-aided manufacturing are increasingly being used by clinicians. With the introduction of new materials, their optical characteristics also need to be investigated.
Purpose:
The purpose of this in vitro study was to compare the translucency and opalescence of lithium disilicate, zirconia-reinforced lithium silicate, presintered zirconia-reinforced lithium silicate, polymer-infiltrated ceramic-network material, and multilayer zirconia.
Material And Methods:
A total of 50 rectangular plates (14×12×1 mm) of 5 monolithic ceramics were prepared in this in vitro study (n=10). Each zirconia specimen was divided into 3 groups of incisal, middle, and gingival thirds. Each group was then evaluated separately. The color parameters of specimens were measured on 3 backgrounds, white, black, and #3 Ivoclar Natural Die Color material, by using a spectrophotometer. The translucency and opalescence of the specimens were determined by the relevant equations, and between-group comparisons were made. One-way ANOVA and Tamhane post hoc tests were used to compare groups (α=.05).
Results:
The difference among the groups was significant in translucency (F=137.346, df=6, P<.001), contrast ratio (F=134.148, df=6, P<.001), and opalescence parameters (F=128.028, df=6, P<.001). The 3 zirconia groups (10.87 ±0.54 to 11.88 ±0.26) had a significantly lower translucency than the other groups, and the zirconia-reinforced lithium silicate group (18.14 ±0.74) showed the highest translucency. Zirconia-reinforced lithium silicate (12.36 ±0.42) had the highest opalescence, and the lowest opalescence was found for polymer-infiltrated ceramic-network (5.43 ±0.28) and the incisal third of zirconia (5.45 ±1.06).
Conclusions:
The zirconia-reinforced lithium silicate and presintered zirconia-reinforced lithium silicate specimens had the highest translucency and opalescence. The studied multilayer zirconia, which had different cubic phase values from incisal to gingival blank, showed similar translucency over the entire range, and differences among different regions were related to chromatic variables.
Related Concept Videos
01:18Porosity in Cement Paste
The balance of water to cement in the mix is...
01:20Porosity and Absorption of Aggregate
When all pores in an aggregate are filled with water, the aggregate is considered saturated and surface-dry. If left in dry air, water will evaporate until the...
01:21Polymer Classification: Crystallinity
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals...