Effects of carbon nanomaterials hybridization of Poly(3,4-ethylenedioxythiophene): poly (styrene sulfonate) on...

The influence of multiple dimensional carbon nanomaterials, such as graphene quantum dots (GQD), multi-walled carbon nanotubes (MWCNT), and graphene sheets (GNS) of the thermoelectric properties in poly(3,4-ethylenedioxythiophene): poly (styrene sulfonate) (PEDOT: PSS)-based hybrids have been investigated. PEDOT: PSS matrix was successfully used to prepare PEDOT: PSS/GQDs (PGQD), PEDOT: PSS/MWCNT (PCNT) and PEDOT: PSS/GNS (PGNS) composite films. According to structural characteristics, strongπ-πinteractions existed between carbon materials and PEDOT: PSS, and PEDOT: PSS layers with organized and arranged morphology were easier templated by GNS than GQD or MWCNT. It was found that besides energy filtering effect, hole-phonon interaction occurred with further addition of GNS and GQDs in PGNS and PGQD composite films. The optimal power factor (PF) of approximately 580 and 103μW m^-1K^-2at 363 K were acquired in PGNS composite films at 5 wt% GNS and PGQD films with 1 wt% GQD filling, respectively. Unlike PGNS and PGQD films, electrical conductivity of PCNT reduced upon the addition of MWCNT, while the Seebeck coefficient decreased firstly, and then increased and reached to the highest value at 10 wt% MWCNT. The optimal PF of 381.8μW m^-1K^-2at 363 K was obtained with weight fraction of 0.1 wt% in PCNT films.