Nitrogen-plasma doping of carbon film for a high-quality layered Si/C composite anode

The effect of the chemical component and microstructure, not to mention their facile modification, of the coating/wrapping carbon layer on the electrochemical performance of the Si/C composite anode in lithium ion batteries (LIBs) hasn't been actively explored although Si/C has been recognized as one of the most promising route for the high energy density LIBs. Herein we propose a novel nitrogen-plasma doping route to modify the top carbon film in an elaborately constructed layered Si/C composite anode. The electrochemical performance, e.g., the initial coulombic efficiency (CE), cycle stability and specific capacity of the composite anode is drastically improved by this plasma processing due to the increased kinetics of lithium ions. By means of the appropriate adjustment of the N doping ratio and N chemical configuration in the carbon layer through a N₂/H₂ plasma processing, the lithium diffusion rate in the composite anode was memorably increased as the pseudocapacitance effects promoted. The optimized Si/C composite exhibits a high capacity of 1120.7 mA h g^-1 and an initial CE of 80.8% at the current of 2 A g^-1 after a long cycle of 1500, increasing by ~40% of specific capacity and ~29% of the initial CE.