Effective recovery of ytterbium through biosorption using crosslinked sericin-alginate beads: A complete continuous...

The recovery of rare-earth from secondary sources is essential for cleaner production. The development of natural biocomposites is promising for this purpose. Sericin is a waste protein from silk manufacturing. The highly polar groups on the surface of sericin facilitate blending and crosslinking with other polymers to produce biocomposites with improved properties. In this work, we investigate ytterbium recovery onto a natural biocomposite based on sericin/alginate/poly(vinyl alcohol) (SAPVA) in packed-bed column, aiming to establish a profitable application for sericin. Effects of flow rate and ytterbium inlet concentration showed that the highest exhaustion biosorption capacity (128.39 mg/g) and lowest mass transfer zone (4.13 cm) were reached under the operating conditions of 0.03 L/h and 87.95 mg/L. Four reusability cycles were performed under the optimum operating conditions using 0.3 mol/L HNO₃. Ytterbium recovery was highly successful; desorption efficiency was higher than 97% and a final ytterbium-rich concentrate (3870 mg/L) was 44 times higher than input concentration. Regenerated beads characterization showed that the cation exchange mechanism plays a major function in continuous biosorption of ytterbium. SAPVA beads also showed higher biosorption/desorption performance for ytterbium than other competing ions. These results suggest the application of SAPVA may be an alternative for large-scale ytterbium recovery.