The stability of Cl-, Br-, and I-passivated Si(100)-(2 × 1) in ambient environments for atomically-precise pattern...

Atomic precision advanced manufacturing (APAM) leverages the highly reactive nature of Si dangling bonds relative to H- or Cl-passivated Si to selectively adsorb precursor molecules into lithographically defined areas with sub-nanometer resolution. Due to the high reactivity of dangling bonds, this process is confined to ultra-high vacuum (UHV) environments, which currently limits its commercialization and broad-based appeal. In this work, we explore the use of halogen adatoms to preserve APAM-derived lithographic patterns outside of UHV to enable facile transfer into real-world commercial processes. Specifically, we examine the stability of H-, Cl-, Br-, and I-passivated Si(100) in inert N₂and ambient environments. Characterization with scanning tunneling microscopy and x-ray photoelectron spectroscopy (XPS) confirmed that each of the fully passivated surfaces were resistant to oxidation in 1 atm of N₂for up to 44 h. Varying levels of surface degradation and contamination were observed upon exposure to the laboratory ambient environment. Characterization byex situXPS after ambient exposures ranging from 15 min to 8 h indicated the Br- and I-passivated Si surfaces were highly resistant to degradation, while Cl-passivated Si showed signs of oxidation within minutes of ambient exposure. As a proof-of-principle demonstration of pattern preservation, a H-passivated Si sample patterned and passivated with independent Cl, Br, I, and bare Si regions was shown to maintain its integrity in all but the bare Si region post-exposure to an N₂environment. The successful demonstration of the preservation of APAM patterns outside of UHV environments opens new possibilities for transporting atomically-precise devices outside of UHV for integrating with non-UHV processes, such as other chemistries and commercial semiconductor device processes.