Collagen Fibres Orientation in the Bone Matrix around Dental Implants: Does the Implant's Thread Design Play a Role?

The aim of this study was to analyse the influence of different thread shapes of titanium dental implant on the bone collagen fibre orientation (BCFO) around loaded implants. Twenty titanium dental implants, divided for thread shapes in six groups (A-F) were analysed in the present study. All implants were immediately loaded and left in function for 6 months before retrieval. The parameters evaluated under scanning electron microscope were the thread width, thread depth, top radius of curvature, flank angle, and the inter-thread straight section. Two undecalcified histological sections were prepared from each implant. Birefringence analysis using circularly polarized light microscopy was used to quantitively measure BCFO. For groups A-F, respectively, transverse BCFO was 32.7%, 24.1%, 22.3%, 18.2%, 32.4%, and 21.2%, longitudinal BCFO was 28.2%, 14.5%, 44.9%, 33.1%, 37.7%, and 40.2%. The percentage differences between transverse and longitudinal orientation were 4.50% (A), 9.60% (B), -22.60% (C), -14.90% (D), -5.30% (E), and -19.00% (F). Following loading, the amount of transverse and longitudinal BCFO were significantly influenced by the thread shape. The greater flank angles and narrower inter-thread sections of the "V" shaped and "concave" shaped implant threads of groups A and B, respectively, promoted the predominance of transverse BCFO, compared to groups C-F (p < 0.05). A narrow inter-thread straight section promotes transverse BCFO, as do "V" shaped and "concave" shaped threads, which can thus be considered desirable design for implant threads.