Improved Surface-Enhanced-Raman Scattering Sensitivity Using Si Nanowires/Silver Nanostructures by a Single Step...

In this study, we developed highly sensitive substrates for Surface-Enhanced-Raman-Scattering (SERS) spectroscopy, consisting of silicon nanowires (SiNWs) decorated by silver nanostructures using single-step Metal Assisted Chemical Etching (MACE). One-step MACE was performed on p-type Si substrates by immersion in AgNO₃/HF aqueous solutions resulting in the formation of SiNWs decorated by either silver aggregates or dendrites. Specifically, dendrites were formed during SiNWs' growth in the etchant solution, whereas aggregates were grown after the removal of the dendrites from the SiNWs in HNO₃ aqueous solution and subsequent re-immersion of the specimens in a AgNO₃/HF aqueous solution by adjusting the growth time to achieve the desired density of silver nanostructures. The dendrites had much larger height than the aggregates. R6G was used as analyte to test the SERS activity of the substrates prepared by the two fabrication processes. The silver aggregates showed a considerably lower limit of detection (LOD) for SERS down to a R6G concentration of 10^-13 M, and much better uniformity in terms of detection in comparison with the silver dendritic structures. Enhancement factors in the range 10⁵-10¹⁰ were calculated, demonstrating very high SERS sensitivities for analytic applications.