Polymeric Microfiltration Membranes Modification by Supercritical Solvent Impregnation-Potential Application in Open...

This study investigated supercritical solvent impregnation of polyamide microfiltration membranes with carvacrol and the potential application of the modified membranes in ventilation of open surgical wounds. The impregnation process was conducted in batch mode at a temperature of 40 °C under pressures of 10, 15, and 20 MPa for contact times from 1 to 6 h. FTIR was applied to confirm the presence of carvacrol on the membrane surface. In the next step, the impact of the modification on the membrane structure was studied using scanning electron and ion beam microscopy and cross-filtration tests. Further, the release of carvacrol in carbon dioxide was determined, and finally, an open thoracic cavity model was applied to evaluate the efficiency of carvacrol-loaded membranes in contamination prevention. Carvacrol loadings of up to 43 wt.% were obtained under the selected operating conditions. The swelling effect was detectable. However, its impact on membrane functionality was minor. An average of 18.3 µg of carvacrol was released from membranes per liter of carbon dioxide for the flow of interest. Membranes with 30-34 wt.% carvacrol were efficient in the open thoracic cavity model applied, reducing the contamination levels by 27% compared to insufflation with standard membranes.